The hydroxy-sulphide yushkinite from the type deposit has been re-examined by electron probe microanalysis and reflectance measurement. The EPMA indicates minor Cu (up to 1.5 wt.%) and confirms an excess of V. Taking into account its composite structure (brucite-like hydroxide layer alternating with a berndtite-type sulphide layer) the proposed structural formula is, with the addition of minor intercalated Cu: [(Mg_0.71Al_0.36V_0.03)_Σ1.10(OH)_2.18O_0.02]Cu_0.02 [VS₂]. At the crystal scale, some crystal edges give a variable excess of Si and Al (in the 1/1 ratio), indicating a late topotactic intergrowth with a layered alumino-silicate (or a composite silicate-sulphide). New specular reflectance data are given in air and oil from 400 to 800 nm, with the polarization plane parallel or perpendicular to the elongation. The refractive index n and absorption coefficient k are given; no absorption band exists in the perpendicular position, with constant n close to 1.9, and k to 0.3. In a parallel position, a pseudo-transparency window is centred around 500–520 nm (∼2.4 eV). The main absorption band, centred around 730 nm (∼1.7 eV), corresponds probably to a transition t_2g → e_g related to intra-layer V-V bonding. Charge transfer from the brucite-type layer to the VS₂ one, strictly controlled through H-bonding, induces a mean formal valency of V close to 3.6. Yushkinite is compared with other synthetic layered hydroxy-sulphides, as well as brucite-type intercalated compounds.